Professional manufacturer of special welding consumablesHIGH TENSILE STRENGTH STEEL ELECTRODE |
|||||||||||||||||||
| Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Mechanical Properties Of Deposited Metal | Application | ||||||||||||
| C | Mn | Si | P | S | Cr | Ni | Mo | V | Others | 屈服强度 Y.P.(MPa) |
T.S.（MPa) | E.L.(%) | I.V.(J) | ||||||
| WS.E9018M | 2.5/3.2/4.0/5.0 | GB/T E6218-N3M1 AWS E9018M |
PA,PB,PC,PD,PE,PF | DC+/AC | 0.058 | 1.02 | 0.37 | 0.024 | 0.011 | 0.13 | 1.66 | 0.33 | 0.01 | - | 690 | 595 | 26 | -50℃/85 | For welding 620MPa grade high strength steel,the coat is iron powder low hydrogen type. |
| WS.E11018M | 2.5/3.2/4.0/5.0 | GB/T E7618-N4M2 AWS E11018M |
PA,PB,PC,PD,PE,PF | DC+/AC | 0.065 | 1.28 | 0.42 | 0.019 | 0.008 | 0.26 | 2.19 | 0.43 | 0.01 | - | 760 | 830 | 20 | -50℃/80 | For welding 760MPa grade high strength steel,the coat is iron powder low hydrogen type. |
HIGH TENSILE STRENGTH STEEL ELECTRODE |
|||||||||||||||||||
| Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Mechanical Properties Of Deposited Metal | Application | ||||||||||||
| C | Mn | Si | P | S | Cr | Ni | Mo | V | Others | 屈服强度 Y.P.(MPa) |
T.S.（MPa) | E.L.(%) | I.V.(J) | ||||||
| WS.E9018M | 2.5/3.2/4.0/5.0 | GB/T E6218-N3M1 AWS E9018M |
PA,PB,PC,PD,PE,PF | DC+/AC | 0.058 | 1.02 | 0.37 | 0.024 | 0.011 | 0.13 | 1.66 | 0.33 | 0.01 | - | 690 | 595 | 26 | -50℃/85 | For welding 620MPa grade high strength steel,the coat is iron powder low hydrogen type. |
| WS.E11018M | 2.5/3.2/4.0/5.0 | GB/T E7618-N4M2 AWS E11018M |
PA,PB,PC,PD,PE,PF | DC+/AC | 0.065 | 1.28 | 0.42 | 0.019 | 0.008 | 0.26 | 2.19 | 0.43 | 0.01 | - | 760 | 830 | 20 | -50℃/80 | For welding 760MPa grade high strength steel,the coat is iron powder low hydrogen type. |